Figure 10: Fracture surface form a specimen welded with a heat input of 40 J/mm (3,300 W, 5 m/min), and tested in fatigue with R = 0.1 and a maximum stress of 850 MPa, which gave a life of 12,565 cycles. Initiation has occurred from a large region of gas porosity.